Potential Alkali Reactivity of Cement-Aggregate Combinations (Mortar-Bar Method). ASTM C Standard Test Method for Potential Alkali Reactivity of Cement- Aggregate Combinations (Mortar-Bar Method). All the Controls products ASTM C standard. Enter now!.
|Published (Last):||22 September 2014|
|PDF File Size:||7.51 Mb|
|ePub File Size:||2.65 Mb|
|Price:||Free* [*Free Regsitration Required]|
Construction Chemistry Directory
Insignificant expansion may result when potentially deleteriously reactive siliceous rocks are present in comparatively high proportion even when a high-alkali cement is used. The method is not recommended as a means to detect the latter reaction because expansions produced in the mortar-bar test by the alkali-carbonate reaction atm Test Method C are generally much less than those produced by the alkali-silica reaction for combinations having equally harmful effects in service.
It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Link to Active This link will always route to the current Active version of the standard. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard.
Sources of such supplementary information include: Dolomitic aggregates that are deleteriously affected by the alkali-carbonate reaction when employed as course aggregate in concrete may not produce notable expansion in this test method. Two types of alkali reactivity of aggregates are recognized: It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Formerly under the jurisdiction of Committee C09 on Concrete and Concrete Aggregates, this test method was withdrawn in October This may occur because the alkali-silica reaction products are characterized by an alkali to silica ratio that is so low as to minimize uptake of water and swelling, or because of alkali leaching from the bars see section on containers.
When it has been concluded from the results of tests performed using this test method and supplementary information as outlined that a given cement-aggregate combination should be considered potentially deleteriously reactive, additional studies may be appropriate to develop information on the potential reactivity of other combinations containing the same cement with other aggregates, the same aggregate ast, other cements, or the same cement-aggregate combination with a mineral admixture.
Two types of alkali reactivity of aggregates are recognized: Criteria to determine potential deleterious alkali-silica reactivity of cement-aggregate combinations from the results of this test method have been given in the Appendix of Specification C The method is not recommended as a cc227 to detect the latter reaction because expansions produced in the mortar-bar astn by the alkali-carbonate reaction see Test Method C are generally much less than those produced by the alkali-silica reaction for combinations having equally harmful effects in service.
Mortar bar container, Cement testing equipment, Controls
Also, significant expansion may occur rarely in the test for reasons other than alkali-aggregate reaction, particularly the presence of sulfates in the aggregate that produce a sulfate attack upon the cement paste, ferrous sulfides pyrite, marcasite, or pyrrhotite that oxidize and hydrate with the release of sulfate, and materials such as free lime CaO or c27 magnesia MgO in the cement or aggregate that progressively hydrate and carbonate.
Data correlating the results of tests performed using this test method with performance of cement-aggregate combinations in concrete in service, results of petrographic examination of aggregates Guide Cand results of tests for potential reactivity of aggregates by chemical cc227 have been published in Test Method C and should be consulted in connection with the use of results of tests performed using this test method as the basis asrm conclusions and recommendations concerning the use of cement-aggregate combinations in concrete.
When expansions in excess of those given in the Appendix of Specification C33 are shown in results of tests performed using this test method, it is strongly recommended that supplementary information ast developed to confirm that the expansion is actually due to alkali reactivity. Stay on Page Continue to Compass.
This test method covered the determination of the susceptibility of cement-aggregate combinations to expansive reactions involving hydroxyl ions associated with the alkalies sodium and potassium by measurement of the increase or decrease in length of mortar bars containing the combination during storage under prescribed conditions. The results of tests performed using this method furnish information on the likelihood that a cement-aggregate combination is potentially capable of harmful alkali-silica reactivity with consequent deleterious expansion of concrete.
This test method is being withdrawn without replacement due to its limited use by industry.